Stainless steel shot, stainless steel cut wire shot, stainless steel polishing shot, stainless steel cut wire shot, mainly used for stainless steel, aluminum alloy die castings, copper alloy surface shot blasting, sandblasting, shot peening, shot peening forming, finishing, strengthening, Matt, correction, retreat paint, to corrosion. Process for the production of stainless steel pill can be divided into two categories, the first category making method is recognized by melting atomization cooling of casting stainless steel pill, English Name: Cast Stainless Steel Shot, class second is made by cutting, polishing of stainless steel is stainless steel pill, stainless steel cut wire shot, stainless steel polishing blasting stainless steel shot, made by second kinds of methods, English named: "Conditioned Stainless Steel Cut Wire Shot", literally translated as: "stainless steel passivation pill", which represents the passivation cylindrical ends edge polishing stainless steel wire; the representative materials; pill on behalf of cut is made. Therefore the German and international standardization organization devoted to the development of production the second kinds of methods: DIN8021-4-1985, SAE product standard AMS 2431/4-1996 Conditioned Stainless Steel Cut Wire Shot, standards and regulations of cylindrical stainless steel cut wire shot after shot after passivation of stainless steel pill sphericity respectively by G1, G2, G3 mark.
Stainless steel pill products are widely used in the surface of aluminum alloy, zinc alloy, copper, stainless steel castings deburring and finishing lighting processing, can improve the anti fatigue, corrosion resistance and cover the surface defects of castings, the product surface whitening, brightening. No damage to the surface, so that the workpiece after processing with fine processing effect.
Chemical composition of carbon ≈ 0.10% chromium ≈ 13% manganese ≈ 1.2% proportion of round pill: 7.9g/cm3 cut microstructure pill:7.8g/cm3 hardness of 400-600HV martensite stainless steel pill name density ≥ 7.7 features: stainless steel spherical particles, is applicable to stainless steel and rare metal castings.